Zn-Ni Alloy Deposit for Cadmium Replacement Applications
IR@CECRI: CSIR-Central Electrochemical Research Institute, Karaikudi
View Archive Info| Field | Value | |
| Title |
Zn-Ni Alloy Deposit for Cadmium Replacement Applications
|
|
| Creator |
Shanmugasigamani , S.
Thangavelu, P.R. Srinivasan, K.N. Selvam, M. |
|
| Subject |
Industrial Metal Finishing
|
|
| Description |
Zinc - nickel alloy was deposited from alkaline bath at a PH of 13-14 with the nickel percentage of 5-9%
in our prior research. Present study dealt with the research on 10-12% of Nickel at a PH of 12-13 from Zinc –
nickel alloy electrolyte and the remaining percentage of Zinc, required for corrosion resistant applications to be used for reliable alternative of cadmium. Hull cell studies was carried out to optimize current density, temperature,
agitation etc., for getting a deposition of 10-12% of Ni & 88-90 % of Zn. SEM, EDAX, XRD measurements
characterize the deposit properties and structure. Corrosion resistance measurements such as polarisation, corrosion
impedance spectra of zinc-nickel alloy were evaluated.
|
|
| Date |
2013-10-02
|
|
| Type |
Article
NonPeerReviewed |
|
| Format |
application/pdf
|
|
| Identifier |
http://cecri.csircentral.net/3071/1/080-2013.pdf
Shanmugasigamani , S. and Thangavelu, P.R. and Srinivasan, K.N. and Selvam, M. (2013) Zn-Ni Alloy Deposit for Cadmium Replacement Applications. INTERNATIONAL JOURNAL OF ENGINEERING SCIENCES & RESEARCH TECHNOLOGY, 2 (10). pp. 3041-3046. ISSN ISSN: 2277-9655 |
|
| Relation |
http: // www.ijesrt.com
http://cecri.csircentral.net/3071/ |
|